Technical Data Sheet
FOR PROFESSIONAL USE ONLY
Product: Automotive Art 2 Pack HS Top Clear 82‐55 Features: It has high solid content Clears, good resistance to weathering and yellowing, good surface hardness. It is matt finish clear. Benefits: Automotive Art 2 Pack HS Top Clear 82‐55 provides matt finish and protection for basecoat paint. It can be mixed with 82‐00 and 82‐50 clear to obtain a semi‐matt finish Recommended Use: For painting passenger and commercial vehicles. 



Materials for the job: Automotive Art HS Top Clear Automotive Art Hardener Automotive Art Reducer Mixing stick, mixing tin and spray gun. 82‐55 30‐ series 35‐series Physical properties: Specific gravity (kg/l): Flash point: Vol.% solids: Coverage: Viscosity (RFU): Gloss: Color: V.O.C. (RTS): 1.01 Closed cup: >15°C (>59°F) approx. 50% 10 m²/L/50 μm (2.0 mil) 18 – 22 sec. Cup DIN 4 matt gloss milky <840 g/l (7.0 lbs/gal) Pretreatment: Apply over Motobase, it may require to pass a light tack cloth over the surface Cleaning the equipment: Lacquer Thinner 6‐051 Shelf Life: Under normal storage conditions minimum two years (unopened tins). If you wish to have a semi‐matt finish, mix with 50% of 82‐00 or 82‐50 clear before mixing with the hardener. 2 : 1 Using mixing stick 100% by vol. Automotive Art top Clear 82‐55 50% by vol. Automotive Art Hardener 30‐ series 0% ‐ 15% by vol. Automotive Art Reducer 35‐ series Gravity gun: HVLP: 1.3 ‐ 1.4 mm High pressure: 1.3 – 1.5 mm Suction gun: HVLP: 1.4 ‐ 1.6 mm High pressure: 1.4 ‐ 1.6 mm Mixing ratio: Hardener Nozzle size: Technical Data Sheet
FOR PROFESSIONAL USE ONLY
Spraying pressure: Application: Total Re‐
spray/Blending in HVLP: 2.0‐2.5 bar (30‐35 p.s.i.) See Info Manufacturer RP 2.5 bar (35 p.s.i.) See Info Manufacturer High pressure: approx. 4 bar (60 p.s.i.) For total re‐spray apply two full coats flash off time of 8 to 10 minutes at 20C (68°F) between coats. For spot blending: refer to blending‐in topcoat Metallics / Solids Coat Thickness: 50 μm (2.0 mil) Drying time: Tack‐free: At 20C(68°F) 2.5 hours 30 minutes At 60C(140°F) 8 minutes IR short wave 10 minutes Polishing: Ready for assembly: 8 hours after cooling Pot life at 20 C(68°F): 4 hours Remarks: Humidity affects clear coat components, so the application equipment should be absolutely dry. Close the hardener container immediately after use. Do not use at temperatures lower than +50ºF/10ºC . In this case, dry in spray booth. 
Was this manual useful for you? yes no
Thank you for your participation!

* Your assessment is very important for improving the work of artificial intelligence, which forms the content of this project

Download PDF

advertisement