Oatey 301402 Specification

Oatey 301402 Specification
H-2095
WATER SOLUBLE TINNING FLUX
TECHNICAL SPECIFICATION: Oatey H-2095 Water Soluble Tinning Flux cleans, tins and fluxes most commonly soldered
metals including copper, brass, zinc, galvanized iron, lead and tin or copper-coated metals. Fluxing is a critical step in the
soldering process. H-2095 Tinning Flux is lead-free and ideal for copper systems including fire sprinkler, hydronic heating,
potable water service and DWV piping. H-2095 Tinning Flux remains active up to 700° F. H-2O95 Flux complies with CA & VT
lead content regulations.
PRECAUTIONS
Read all cautions and directions carefully before using this
product. Apply flux with brush- do not apply with fingers.
Wash thoroughly after handling and before eating. Eye/Skin
contact may cause intense irritation and injury. In case of
eye/skin contact, flush freely with water and seek medical
attention immediately. If swallowed, DO NOT INDUCE
VOMITING, drink water and call a physician or poison control
center immediately. Ingestion of this product could cause
gastrointestinal distress. DO NOT REUSE EMPTY
CONTAINER. KEEP OUT OF REACH OF CHILDREN.
Refer to material safety data sheet for more information.
For emergency first aid help, call 1-877-740-5015.
COMMON APPLICATIONS
Oatey H-2095 Water Soluble Tinning Flux can be used to
solder most commonly soldered metals including copper,
brass, zinc, galvanized iron and tin or copper-coated metals.
PHYSICAL/CHEMICAL
Appearance
Shelf Life
pH
Solder Temp. Range
PROPERTIES
Greenish-Gray Paste
1 year from manufacture date
3-4
400-700 F
DIRECTIONS FOR USE
Paste Fluxes require only a small amount of flux applied
to the joint. Clean all surfaces before soldering. Apply
small amount of flux inside the fitting and outside of the
pipe. Heat to temperature required for soldering. Do not
overheat the piping. For small diameter piping, direct
the heat near the joint. For large diameter piping, move
the heat around the joint to ensure adequate solder flow
around the circumference of the joint. NOT FOR USE
WITH ALUMINUM, STAINLESS STEEL OR MAGNESIUM.
DO NOT USE ON ELECTRICAL PARTS.
When soldering process is complete, allow joint to cool
undisturbed. Remove any flux residual with a damp
cloth. Do not store H-2095 Tinning Flux above 120° F.
Consult Oatey Technical Department for applications not
specifically referenced above.
INGREDIENTS (CAS Number)
Triethanolamine Hydrochloride (637-39-8)
Zinc Chloride (7646-85-7)
Ammonium Chloride (12125-02-9)
Surfactant Blend (N/A)
Inert Fillers (N/A)
Tin (7440-31-5)
Copper (7440-50-8)
Bismuth (7440-69-9)
COMPLIANCE AND LISTINGS
NSF Listed to
Standard 61
Lead Free Flux
Complies with CA & VT lead legislation
Flux Base meets ASTM Standard B 813
PRODUCT
NUMBER
30140
30142
30143
53068
C-2
DESCRIPTION
PACK
1.7 oz. H-2095 Water Soluble Tinning Flux
8 oz. H-2095 Water Soluble Tinning Flux
16 oz. H-2095 Water Soluble Tinning Flux
1.7 oz. H-2095 Water Soluble Tinning Flux with Brush – Carded
12
24
24
12
Visit www.oatey.com for updates
CARTON
WEIGHT
4 lbs.
16 lbs.
15 lbs.
2 lbs.
1/2010